MEGASID Transparent polyester resin. is a transparent polyester-based resin for metal, plastic and fiberglass. Colorless and light stable, suitable for bonding and repairing damaged or gaps, it is also used for application with fiberglass fabric. Levante Polyester Resin is equipped with a liquid catalyst, to be added at a rate of 3%.

CATALYSIS: from 3% to a maximum of 5%

GEL TIME: 9-12 minutes

EXOTHERMAL PEAK: 180-190 C at 15-17 minutesi

Application:

- Prepare the surface to be treated by cleaning it from grease and salt;

- Add its hardener to the resin, in the ratio of 3 5%, and mix the two welle

components;

- Apply by brush; the product can be processed after complete catalysis;

- Do not apply on damp surfaces.

Features:

 Specific weight 1100 20 g / ll

Solid by weight 64 2%%

Viscosity 850 100 cPP

Barcol hardness 47

Tensile strength 54 MPa

Flexural strength 99 MPa

Tensile modulus of elasticity 3728 MPa

Flexural modulus 3328 MPa

Yield strength 110 MPa

Maximum breaking load 269 MPa

Hazard label:

UFI Code: TF30-601R-600A-ANRU

Hazard statements:

H226 Flammable liquid and vapor. H361d Suspected of damaging the unborn child. H372 Causes damage to organs through prolonged or repeated exposure. H319 Causes serious eye irritation. H315 Causes skin irritation. H335 May cause respiratory irritation. H317 May cause an allergic skin reaction. H412 Harmful to aquatic life with long lasting effects.

Precautionary advice:

P201 Obtain special instructions before use. P210 Keep away from heat sources, hot surfaces, sparks, open flames or other sources of ignition. Not smoking. P260 Do not breathe dust / fume / gas / mist / vapors / spray. P280 Wear protective gloves and eye / face protection. P308 + P313 IF exposed or likely to be exposed, seek medical attention.

P370 + P378 In case of fire: use carbon dioxide, foam, chemical powder to extinguish. Contains: COBALT STYRENE BIS (2-ETHYLESANOATE)

VOC (Directive 2010/75 / EC): 38.00% - 418.00 g / liter

 VOC (volatile carbon): 35.03% - 385.29 g / liter