Two-component Polyurethane Enamel Color 2K Matt Glossy RAL 1 KG
Color select according to the chosen tint

Two-component Polyurethane Enamel Color 2K Matt Glossy RAL 1 KG
BLACK - WHITE
Punto Vendita Net Coatings
Via Emilia 2
35043 Monselice PD
Italy
RAL 1035, RAL 1036, RAL 2013, RAL 3032, RAL 3033, RAL 4011, RAL 4012, RAL 5025, RAL 5026, RAL 6035, RAL 6036, RAL 7048, RAL 8029, RAL 9022, RAL 9023, RAL 1026, RAL 2005, RAL 2007, RAL 3024, RAL 3026, RAL 6038
Megasid line POLIURSID two-component enamel based on polyurethane resins recommended for quality finishes for fine metal furniture,
household appliances, scientific instruments, decorative indoor panels, machine tools and automatic packaging machines, trucks, tankers, earth-moving machines, automatic machines, agricultural machines, reinforced polyester products, and much more.
Film form with a pleasant appearance, hard and elastic with excellent resistance characteristics to fuels, lubricants, chemical agents, and detergents; it also has good resistance to weathering and yellowing.
Available in the following finishes: Glossy, Semi-glossy, Semi-matte, and Matte.
Price per KG, each kit contains Catalyst, thinner sold separately CLICK HERE FOR THE THINNER
POLIURSID can be applied not only with traditional guns (nozzle from 1.3 up to 1.5mm) but also with mixed air or airless systems, brush, and roller.
Lower temperatures delay drying, while much higher temperatures can cause surface defects.
The enamels in question must be applied fluidly and in a thin layer, as the high solid content ensures full and glossy films with only two coats.
Insufficient thinning can cause film imperfections (small blisters or craters).
It is advisable that the air drying of POLIURSID enamels occurs at an air temperature of about 20°C and with not too high humidity.
These enamels are always recoatable, but after more than 24 hours of air drying or after accelerated drying in an oven, a light sanding is recommended before recoating.
Cycle:
A pretreatment with Megasid epoxy primer is recommended.
Technical data:
Solid Content (w/w): 66.4 ± 1 %
Viscosity (DIN4/25°C): 30 - 180 sec
Pot Life: 4-6 hours at 25°C
Theoretical Yield:
at 30 Microns: 10 sqm ± by spray, for brush and roller approximately 30% loss
Thinning:
Up to a maximum of 50% by weight with polyurethane thinner NC 170
Catalysis:
For Glossy: 50% by weight with POLIURSID catalyst
For Semi-gloss, Semi-matte, and Matte: 30% by weight with POLIURSID catalyst
Incorrect catalysis can irreversibly compromise the color appearance and drying time.
Once catalyzed, do not close the can under any circumstances.
Drying:
Dust-free: 30-40 minutes
Touch dry: 3-5 hours
Through dry: 24 hours
Maximum film resistance is achieved after 7-8 days.
Catalyst jar: FE40 - Iron collection
Catalyst cap and seal: HDPE04 - Plastic collection
Check your municipality's regulations.
Dispose of only if perfectly clean.