Megasid Bicomponent Putty For Fiberglass Fiberglass 1,5kg + Catalyst

The two-component MEGASID FIBERGLASS putty is a spatula putty formulated with a high percentage of glass fiber suitable, therefore, for the reconstruction of missing parts in the car bodywork and for plastic parts, such as bumpers, fiberglass tanks, etc. The product is very spreadable and sandable, thus making it absolutely incomparable in restoration work.

MEGASID FIBERGLASS can be painted with any type of primer, single or two-component.

Available in 250 g version Click here.

TECHNICAL DATA:

Specific weight	1680 20g/mll		1680 20g/mll	(MI 001)
V.O.C.	60 2 g/ll		62 2 g/ll	(ASTM 2369)
Viscosity	950 100 Passs		1600 100 Passs	(MI 002B; 25C))
Consistency	870 100 Passs		1100 100 Passs	(MI 002B; 25C))
Color		Dark green, black			Light green

 

APPLICATION:

− Make sure that the surfaces to be grouted are perfectly dry and clean, in case of application on bare sheet metal, sand it with P 80 and P 150 abrasive papers;

− Take the quantity to use from the jar with clean tools, adding 1 - 3 grams of hardener for every 100 grams of product;

− Mix this quantity by amalgamating the two components well;

− Apply the filler on the surface to be worked on, bearing in mind that the product can be sanded (dry P 80 P 120 grit) after about 30 - 40 minutes; the hardening times can be altered according to the ambient temperature: they shorten with temperatures above 25 C and lengthen with lower temperatures;i;

− Do not put catalysed and/or unused grout back into the can to prevent the entire contents of the can from deteriorating;

− Close the jar after use, in order to prevent the product from hardening in contact with air.

DATA:

Application: Spatula

Catalysis: 1 3 %%

Gel Time: 5-7 Minutes at 25CC

Outside Footprint: 10-30 Minutes at 25CC

Complete Drying: <1 Hour at 25CC

Sandable: After 30-40 minutes at 25CC

Disposal:

Jar: FE40 - Iron Collection

Cap: HDPE2 - Plastic collection.

Recycle only if perfectly clean and empty.

Otherwise recycle on special ecological centers.

Hazard label:

UFI STUCCO CODE:

 

H226Flammable liquid and vapour.

H361dSuspected of damaging the unborn child.

H372Causes damage to organs through prolonged or repeated exposure.

H319Causes serious eye irritation.

H315Causes skin irritation.

P201 Obtain special instructions before use.

P210Keep away from heat, hot surfaces, sparks, open flames and other ignition sources. Not smoking.

P260Do not breathe dust / fume / gas / mist / vapors / spray

P280Protect eyes / face.

P308+P313IF exposed or concerned, get medical advice/attention.

P370+P378In case of fire: Use carbon dioxide, foam, chemical powder to extinguish.

Contains: STYRENE

 

VOC (Directive 2004/42/EC)

VOC expressed in g/litre of ready-to-use product: 62.00

Maximum limit: 250.00

APPLICATION:
− Make sure that the surfaces to be filled are perfectly dry and clean; if applying on bare metal, sand it with abrasive papers P 80 and P 150;
− Take the amount to use from the jar with clean tools, adding 1 - 3 grams of hardener for every 100 grams of product;
− Mix this amount well, combining the two components;
− Apply the filler to the surface to be worked on, keeping in mind that the product can be sanded (grit P 80 – P 120 dry) after about 30 - 40 minutes; curing times may vary depending on the ambient temperature: they shorten with temperatures above 25 °C and lengthen with lower temperatures;
− Do not return catalyzed and/or unused filler to the jar to avoid deteriorating the entire contents of the jar;
− Close the jar after use to prevent the product from hardening upon contact with air.
DATA:
Application: Spatula
Catalysis: 1 – 3 %
Gel Time: 5-7 Minutes at 25°C
Out of Print: 10-30 Minutes at 25°C
Complete Drying: <1 Hour at 25°C
Sandable: After 30-40 minutes at 25°C