MEGASID Transparent polyester resin. is a transparent polyester-based resin, for metal, plastic and fiberglass. Colorless and light-stable, suitable for gluing and repairing damaged or incomplete parts, it is also used for application with fiberglass fabric. Levante Polyester Resin is accompanied by a liquid catalyst, to be added at a rate of 3%.

CATALYSIS: from 3% to a maximum of 5%

GEL TIME: 9-12 minutes

EXOTHERMAL PEAK: 180-190 C for 15-17 minutesi

Application:

- Prepare the surface to be treated by cleaning it from grease and salt;

- Add its hardener to the resin, at a rate of 3 5%, and mix the two welle

components;

- Apply with a brush; the product can be processed after complete curing;

- Do not apply on damp surfaces.

Features:

 Specific weight 1100 20 g/ll

Solids by weight 64 2 %%

Viscosity 850 100 cPP

Hardness Barcol 47

Tensile strength 54MPa

Flexural strength 99 MPa

Tensile modulus of elasticity 3728 MPa

Flexural modulus 3328 MPa

Yield strength 110 MPa

Maximum breaking strength 269 MPa

Hazard label:

UFI code: TF30-601R-600A-ANRU

Indications of danger:

H226 Flammable liquid and vapour. H361d Suspected of damaging the unborn child. H372 Causes damage to organs through prolonged or repeated exposure. H319 Causes serious eye irritation. H315 Causes skin irritation. H335 May cause respiratory irritation. H317 May cause an allergic skin reaction. H412 Harmful to aquatic life with long lasting effects.

Precautionary statements:

P201 Obtain special instructions before use. P210 Keep away from heat, hot surfaces, sparks, open flames and other ignition sources. Not smoking. P260 Do not breathe dust / fume / gas / mist / vapors / spray. P280 Wear protective gloves and eye/face protection. P308+P313 IF exposed or concerned: Get medical advice/attention.

P370+P378 In case of fire: Use carbon dioxide, foam, chemical powder to extinguish. Contains: COBALT STYRENE BIS(2-ETHYLHEXANOATE).

VOC (Directive 2010/75/CE) : 38,00 % - 418,00 g/litre

 VOC (volatile carbon): 35.03% - 385.29 g/litre